Evaluate the Solubility of PMMA Denture Base Material Incorporated with Zeolites Loaded with Transition Elements

  • Mayada M. Ali Department of Basic Sciences, College of Dentistry, University of Mosul, Iraq
  • Ammar A. Qasim Department of Basic Sciences, College of Dentistry, University of Mosul, Iraq
  • Raghed Y. Ghazal Department of Chemistry, College of Education, University of Mosul, Iraq
Keywords: PMMA Solubility, Poly acrylates, Denture Base Material Properties, Loading Materials & Zeolites

Abstract

Aim: Determine the effect of incorporating of zeolites loaded with transitional elements on the solubility of dentures base materials. Material and Methods: The process of preparing zeolites were carried out in laboratory of industrial chemistry in the education college at Mosul university, also the polymerization process for PMMA were carried out according to manufacturer instructions, after that; the PMMA were loaded with transition elements; ( silver , copper and nickel) at different concentrations, the proportions were (2%, 3% and 5% ) and with several elements at fixed concentration in the dentistry college at Mosul university. Results: the solubility values showed that the zeolite denture base material loaded with silver was the best compared to others elements, the bests proportion (2%) foe silver compared others proportions. Conclusion: The incorporation of zeolite for the transitional elements as a whole led to an increase in the solubility of the PMMA denture base material.

References

1. Mohammed M Gad, Shaimaa M Fouda, Fahad A Al-Harbi, Ritva Näpänkangas, and Aune Raustia PMMA denture base material enhancement: a review of fiber, filler, and Nano filler addition, Int. J Nanomedicine.2017;12: 3801–3812.
2. Farhang M., Fariba S., Fereydoon P., Vahedeh G., Yousef K. and Mahsa T. Effect of the denture cleaning agents on tensile and shear ond strengths of soft liners to acrylic denture base.2017 J Dent Res Dent Clin. Dent Prospects. v.11(3); 183–188
3. Zafar M. S. Prosthodontic Applications of Polymethyl Methacrylate (PMMA) Polymers. 2020;12, 2299.
4. Dinesh R.,Viritpon S., Janak S., Jiaqian Q., Krisana S., Vilailuck S.Polymeric materials and films in dentistry: An overview Journal of Advanced Research. 2018; Volume 14:25-34.
5. Rama, K. A., Suresh, S., Venkata, R. A., Kishore, G. & Nagaraj, U Influence of Fibre Reinforcement on the Properties of Denture Base Resins. Journal of Biomaterials and Nanobiotechnology. 2013; 4: 91-97.
6. Rajul, V. & Romesh, S Denture Base Materials: Some Relevant Properties and their Determination. International Journal of Dentistry and Oral Health.2015; 1(4):1-3.
7. Sheng, T. J., Shafee, M. F., Ariffin, Z. and Jaafar, M Review on poly-methyl methacrylate as denture base materials, Malaysian Journal of Microscopy vol.2018;14:1-16.
8. Carmen L., Beniamino P Zeolite: “the magic stone”; main nutritional, environmental, experimental, and clinical fields of application. Nutr Hosp. 2015; 32(2):573-581.
9. Purnomo, Putu H. S., Dwi S Zeolite-Based Biomaterials for Biomedical Application: A Review. AIP Conference Proceedings . 2018;Vol.1977, Issue 1, https://doi.org/10.1063/1.5042933.
10. Jessica Hao, Spencer Lang, Francis Mante, Kresimir Pavelić, and Fusun Ozer Antimicrobial and Mechanical Effects of Zeolite Use in Dental Materials A Systematic Review Acta Stomatol Croat. 2021; 55(1): 76–89.
11. Mohammad S., Negin G., Naser A., Baharak D., Yasamin G., Sajjad S Zeolite-silver-zinc nanoparticles: Biocompatibility and their effect on the compressive strength of mineral trioxide aggregate, J Clin Exp. Dent. 2017; 9(3): e356–e360.
12. Derakhshankhah H, Jafari S, Sarvari S, Barzegari E, Moakedi F, Ghorbani M, Shiri Varnamkhasti B, Jaymand M, Izadi Z, Tayebi L Biomedical Applications of Zeolitic Nanoparticles, with an Emphasis on Medical Interventions, International Journal of Nanomedicine. 2020;Vol.:15:363-386.
13. Zainab A. A., Nabeel A. F. The effect of incorporation of prepared Ag-Zn Zeolite on some properties of heat polymerized acrylic denture base materials. J Bagh. Col., Dent. 2015;Vol. 27(1):63-69
14. Wafaa A. H., Furqan S. H. The Effect of Additives on Denture Base Resin Properties, J. Al-Nah Univ. 2017; Vol.20(4):44-50.
15. Victoria B.R., Camilo A. L., Manuela H. M., Olga G. P. Nanomaterials in Dentistry: State of the Art and Future Challenges. Nanomaterials. 2020;10, 1770:1-24.
16. Arwa A. H., Mohammad R. K., and Hafez I. B. Effect Of Reinforcement of Acrylic Resin By Nanosilver And Nanogold on Water Sorption and Solubility, Az.JDSci.2018;Vol.21,(2):55-159.
17. Huda A. S. Israa M.H. Water sorption and solubility of the acrylic soft liner after incorporation of silver-zinc Zeolite.5th Inter. Sci., Conf.,Med., Health, Special., 408Session Tow (DT). 2020:9-110.
18. Cevik, P., Yildirim B., A.Z.The effect of silica and prepolymer nanoparticles on the mechanical properties of denture base acrylic resin. Journal of prosthodontics. 2018;27(8):763-770.
19. Yousheng T. Hirofumi K. Lioyd A. Katsumi K. Mesopore-Modified Zeolite: Preparation Characterization, and Applications.Chem.Rev.2006;106:896-910.
20. Auwal, I. A., Wong, K. L., Ling, T. C., Ooi, B. S., Ng, E. P. Metal chlorides grafted on SAPO-5 (MClx/SAPO-5) as reusable and superior catalysts for acylation of 2-methyl furan under non-microwave instant heating conditions. Processes 2020, 8(5), 603.
21. Sadoon,M.M. The effect of different nanoparticles incorporation on some properties of the acrylic-based soft liner, Mosul Univ., PhD thesis, 2021.
22. Al-Ali. A.A. Synthesis and study of new Copolymers of Acrylic Resin Denture Base Materials, Mosul Univ., PhD thesis, 2017.
23. Rosana M.S. F., Bruna. C., César A. G. A., Carolina Y. C. S., Vanessa M. U., Karin. H. N. Porosity, water sorption and solubility of denture base acrylic resins polymerized conventionally or in the microwave.JAppl.Oral.Sci.2018; 26:e20170383.
Published
2023-05-31
How to Cite
Ali, M. M., Qasim , A. A., & Ghazal, R. Y. (2023). Evaluate the Solubility of PMMA Denture Base Material Incorporated with Zeolites Loaded with Transition Elements. Central Asian Journal of Medical and Natural Science, 4(2), 486-496. Retrieved from https://cajmns.centralasianstudies.org/index.php/CAJMNS/article/view/1450
Section
Articles